| REFERANS | N341500 |
|---|---|
| TÜR | ABD KARAR (CROSS) |
| GTİP | 3907.99.50.50 |
| KISA TANIM | PBAT bileşiği plastik hammadde peleti. |
| TANIM | ÜRÜN, PBAT BILEŞIĞI OLARAK ADLANDIRILIR. ÜRÜN, %70 PBAT, %10 POLILAKTIK ASIT (PLA), %15 KALSIYUM KARBONAT (CACO3) VE %5 TALK'TAN OLUŞAN BIR KOPOLIMER OLARAK ADLANDIRILIR. PBAT BILEŞIĞININ ANA HEDEF UYGULAMALARI PLASTIK TORBALAR, MALÇ FILMLERI VE GIDA AMBALAJLARIDIR. PBAT NEAT ÇIN'DEN GÜNEY KORE'YE GÖNDERILMIŞTIR. GÜNEY KORE'DE, PBAT NEAT ÖLÇÜLÜR VE KARIŞTIRICIYA EKLENIR. PLA TAYLAND'DAN, TALK HINDISTAN VEYA PAKISTAN'DAN KAYNAKLANIR VE DIĞER KATKI MADDELERI ÖLÇÜLÜR VE KARIŞTIRICIYA EKLENIR. BILEŞENLER BIRBIRINE KARIŞTIRILIR. GÜNEY KORE'DEN KAYNAKLANAN CACO3 ÖLÇÜLÜR VE AYRI BIR YAN HAZNEYE EKLENIR. PBAT, PLA, TALK KARIŞIMI EKSTRUDERIN ANA BESLEYICISINE BESLENIR. CACO3 EKSTRUDERIN YAN BESLEYICISI ARACILIĞIYLA BESLENIR. EKSTRUDERDE MALZEMELER BELIRLI BIR SICAKLIK VE BASINÇ ALTINDA EŞIT OLARAK KARIŞTIRILIR. ELDE EDILEN ÜRÜN, %70 PBAT, %10 PLA, %15 CACO3 VE %5 TALK'DAN OLUŞAN PBAT BILEŞIĞIDIR. ÜRÜN SOĞUTULUR VE EŞIT BOYUTTA PELETLER HALINDE KESILIR. ÜRÜN DAHA SONRA, HERHANGI BIR NEM IÇERIĞINI GIDERMEK IÇIN NEM ALMA VE KURUTMA IŞLEMLERINE GIDERILIR, INCELENIR VE BELIRTILEN AĞIRLIK BIRIMLERIYLE PAKETLENIR. PBAT BILEŞIĞI IÇIN UYGULANABILIR ALT BAŞLIK, BIRLEŞIK DEVLETLER'IN UYUMLU TARIFE TARIFESI (HTSUS) OLACAKTIR. BU TARIFE TARIFESI, DIĞER POLIESTERLERI, BIRINCIL FORMLARDA, ŞUNLARI SAĞLAR: DIĞER: DIĞER: DIĞER. GENEL GÖREV ORANI AD VALOREM OLARAK YÜZDE 6,5 OLACAKTIR. |
| BAŞLANGIÇ TARİHİ | 14.08.2024 |
| BİTİŞ TARİHİ | |
| YABANCI TANIM | THE PRODUCT UNDER CONSIDERATION IS REFERRED TO AS PBAT COMPOUND. THE PRODUCT IS REFERRED TO AS A COPOLYMER COMPOSED OF 70 PERCENT PBAT, 10 PERCENT POLYLACTIC ACID (PLA), 15 PERCENT CALCIUM CARBONATE (CACO3) AND 5 PERCENT TALC. THE PRIMARY TARGET APPLICATIONS OF THE PBAT COMPOUND ARE PLASTIC BAGS, MULCH FILMS AND FOOD PACKAGING. PBAT NEAT IS SHIPPED FROM CHINA TO SOUTH KOREA. IN SOUTH KOREA, THE PBAT NEAT IS MEASURED AND ADDED TO THE MIXER. PLA SOURCED FROM THAILAND, TALC SOURCED FROM INDIA OR PAKISTAN AND OTHER ADDITIVES ARE MEASURED AND ADDED TO THE MIXER. THE COMPONENTS ARE MIXED TOGETHER. CACO3 SOURCED IN SOUTH KOREA IS MEASURED OUT AND ADDED TO A SEPARATE SIDE HOPPER. THE PBAT, PLA, TALC BLEND IS FED INTO THE EXTRUDER’S MAIN FEEDER. THE CACO3 IS FED INTO THE EXTRUDER VIA THE SIDE FEEDER. IN THE EXTRUDER THE MATERIALS ARE UNIFORMLY BLENDED UNDER A SPECIFIED TEMPERATURE AND PRESSURE. THE RESULTING PRODUCT IS PBAT COMPOUND COMPOSED OF 70 PERCENT PBAT, 10 PERCENT PLA, 15 PERCENT CACO3 AND 5 PERCENT TALC. THE PRODUCT IS COOLED AND CUT INTO PELLETS OF UNIFORM SIZE. THE PRODUCT THEN UNDERGOES DEHUMIDIFICATION AND DRYING TO REMOVE ANY MOISTURE CONTENT, IS INSPECTED AND PACKAGED IN UNITS OF SPECIFIED WEIGHT. THE APPLICABLE SUBHEADING FOR THE PBAT COMPOUND WILL BE 3907.99.5050 , HARMONIZED TARIFF SCHEDULE OF THE UNITED STATES (HTSUS), WHICH PROVIDES FOR OTHER POLYESTERS, IN PRIMARY FORMS: OTHER: OTHER: OTHER. THE GENERAL RATE OF DUTY WILL BE 6.5 PERCENT AD VALOREM. |
Otomatik gümrük beyanname kontrolü |
Yapay zeka ile fatura okuma |
Yapay zeka ile gtip tahmini |
Gümrük müşavir programı |
Yapay zeka ile gtip tahmini |
Gümrük müşavir portalı |
Gümrük beyanname takip sistemi |
Gümrük ceza takip sistemi |
Email takip sistemi |
İthal ürün takip sistemi |
İhracat fatura takip sistemi |
Muhasebe denetim sistemi |
Sonradan kontrol sistemi |
Telafi edici vergi hesaplama